A preliminary study of hardness and modulus of elasticity in sheep mandibles submitted to distraction osteogenesis and low-level laser therapy
2011
Objectives: To investigate the quality of newly formed bone in sheep mandibles submitted to distraction osteogenesis and low-level laser therapy (LLLT), based on hardness and modulus of elasticity values. The ideal moment for laser application (during the latency/activation period vs. during the bone consolidation period) was also evaluated. Computed tomography imaging was used to assess relapse as a result of early device removal. Study design: Extraoral distraction devices were placed in five sheep so as to achieve 1.5 cm of lengthened bone in 60 days. Distraction devices were removed 50, 40, and 33 days after surgery. Four animals were treated with LLLT, at different times, and one was u…
Effect of alloy type and casting technique on the fracture strength of implant-cemented structures.
2010
Objectives: To evaluate the influence of alloy type and casting procedure on the fracture strength (FS) of metallic frameworks for implant-supported fixed prostheses. Study design: Thirty three-unit structures for lower posterior bridges were waxed-up and randomly assigned to two groups (n=15) according to alloy type and casting technique: Group 1 (C): cobalt-chromium cast in a centrifugal machine (TS1, Degussa-Hüls); Group 2 (T): titanium cast in a pressure-differential device (Cyclarc II, Morita). Each structure was cemented onto two prefabricated abutments under a constant seating pressure. After 6 months of water aging, samples were loaded in a static universal testing machine (EFH/5/FR…
Physical-mechanical effects of Nd:YAG laser on the surface of sound dental enamel.
1993
Human dental enamel samples were irradiated using a 5 kHz Q-Switched Nd:YAG laser. An increase in Knoop microhardness and modification of the membrane permselectivity were detached. These results and the changes observed by SEM, can be connected with the fusion of the enamel surface.
Light transmittance of zirconia as a function of thickness and microhardness of resin cements under different thicknesses of zirconia
2012
Objective: The objective of this study was to compare microhardness of resin cements under different thicknesses of zirconia and the light transmittance of zirconia as a function of thickness. Study design: A total of 126 disc-shaped specimens (2 mm in height and 5 mm in diameter) were prepared from dual-cured resin cements (RelyX Unicem, Panavia F and Clearfil SA cement). Photoactivation was performed by using quartz tungsten halogen and light emitting diode light curing units under different thicknesses of zirconia. Then the specimens (n=7/per group) were stored in dry conditions in total dark at 37°C for 24 h. The Vicker's hardness test was performed on the resin cement layer with a micr…
Microhardness of different resin cement shades inside the root canal
2012
Objectives: To compare microhardness along the root canal post space of two resin cements in different shades and a dual-cure resin core material. Study Design: Root canals of 21 bovine incisors were prepared for post space. Translucent posts (X•Post, Dentsply DeTrey) were luted using one the following resin luting agent: Calibra (Dentsply DeTrey) in Translucent, Medium and Opaque shades, RelyX Unicem (3M ESPE) in Translucent, A2 and A3 shades and the dual-cure resin core material Core•X flow. All materials were applied according to manufacturers’ instructions and were all photopolymerized (Bluephase LED unit, Ivoclar Vivadent, 40s). After 24 hours, roots were transversally cut into 9 slice…
Mechanical Properties of Pore-Spanning Lipid Bilayers Probed by Atomic Force Microscopy
2006
AbstractWe measure the elastic response of a free-standing lipid membrane to a local indentation by using an atomic force microscope. Starting point is a planar gold-coated alumina substrate with a chemisorbed 3-mercaptopropionic acid monolayer displaying circular pores of very well defined and tunable size, over which bilayers composed of N,N,-dimethyl-N,N,-dioctadecylammonium bromide or 1,2-dioleoyl-3-trimethylammonium-propane chloride were spread. Centrally indenting these “nanodrums” with an atomic force microscope tip yields force-indentation curves, which we quantitatively analyze by solving the corresponding shape equations of continuum curvature elasticity. Since the measured respon…